EN32B Steel Round Bar, EN32B Steel Round Bar Manufacturers, EN32B Steel Suppliers, EN32B Stockist, EN32B Steel Dealers, EN32B Steel Distributors, EN32B Wholesalers, EN32B Steel Traders, EN32B Steel Square Distributors, EN32B Steel Flat Bar, EN32B Steel Companies Near me.

 

Grade Introduction:

EN32B is a carbon case hardening steel. Components when carburized have a core strength range of 430-490 N/mm2, with a hard-wearing surface. It is a popular case hardening steel grade for general engineering, readily machinable and weldable in its supply condition. EN32B is low tensile steel suited for lightly stressed components.

 

Grade Application:

Commonly used for general engineering lightly stressed applications that are subject to wear, EN32B is suitable for applications such as collets, cams, rollers, bushes, spindles, and gears.

 

Equivalent grades:

DIN	CK15
IS	C14
EN	EN32B
SAE/AISI	1015, 1016, 1018
SAE	SAE1015CHQ
IS	C15Mn75
Wnr	1.1141
DIN	C15
USA	1015,1016
BS	040A15

 

Addition to other grades:

MS, EN1A, EN3B, EN8, EN8D, EN9, EN19, EN24, EN31, EN36C, EN41B, EN43B, EN47, EN353, IS2062, 42Crmo4, OHNS, HCHCR, D2, D3, H-11, H-13, CW-1, M2, M35, M42, 2714, SKD-11, P20, P20+S, P20+Ni, SCM 420, ASTM SA-36, ASTM SA-105, SAE 1018, SAE 1020, SAE 4140, SAE 8620, 16MNCR5, 20MNCR5, C20, C35, C40, C45, C50, C60, CK45, 20C8, 40C8, 45C8, 55C8, C55MN75, SAE 52100, S40C, S355J2G3.

 

Our Supply Range:

 

Price List:

 

People also search as:

EN32B, EN32B Steel, EN32B Chemical composition, EN32B Mechanical properties, EN32B Equivalent Grades, EN32B Steel plate, EN32B Steel sheet, EN32B Manufactures, EN32B Suppliers, EN32B Dealers, EN32B Stockist, EN32B Distributors, EN32B Wholesalers, EN32B Traders.

 

Chemical composition:

The following table shows the chemical composition of EN32B steel:

Element	C	Si	Mn	P	S
Carbon(%)	0.13-0.18	0.10-0.40	0.70-0.90	0.05 Max	0.05 Max

 

Mechanical Properties:

Tensile Strength	Elongation	Impact	Impact	Test Piece
Rm N/mm2	percent 5.665ÖSo	Izod J	KCV J	Size
490 460 430	16 16 18	30 30 30	35 35 35	13 19 29

 

Hardness:

 

Heat treatment:

Heat treatment temperatures, including the rate of heating, cooling, and soaking times will vary due to factors such as the shape and size of each steel component. Other considerations during the heat treatment process include the type of furnace, quenching medium, and workpiece transfer facilities.

 

Hardening:

Harden at a temperature of 760-780°C. Quench in water.

 

Tempering:

Tempering is recommended for stress relief and maximum case toughness. Tempering ranges from 150-200°C.

 

Physical Properties:

 

Thermal Properties:

THERMAL PROPERTIES	METRIC	IMPERIAL
Thermal conductivity	51.9 W/mK	360 BTU in/hr.ft².°F

 

Forging Properties:

Heat slowly and uniformly to 1100°C. After forging cool slowly.

 

Stress Reliving:

After rough machining tools should be stress relieved. Soaking time 2 hours after the whole piece has attained a temperature of approximately 675°C. Cool in a furnace to approximately 500°C, and then freely in the air.

 

Normalizing:

Normalize at 840-870°C, and cool in air.

 

Annealing:

Heat uniformly to 700°C. Soak well and cool slowly in the furnace.

 

Density:

 

Machinability:

 

Welding:

 

Supply Cities:

Ahmedabad, Amaravathi, Ambattur, Bangalore, Belgaum, Chennai, Chittoor, Coimbatore, Dindigul, Mysore, Nellore, Hyderabad, Kochi, Mangalore, Tirupur, Tuticorin, Madurai, Andhra Pradesh, Karnataka, Puducherry, Kerala, Tamil Nadu, Telangana, Salem, Thanjavur, Trichy, Erode, Vellore, Ranipet, Sivakasi, Karur, Hosur, Nagercoil, Kanchipuram, Karaikudi, Neyveli, Cuddalore, Kumbakonam, Thiruvannamalai, Pollachi, Rajapalayam, Gudiyatham, Pudukottai, Vaniyambadi, Ambur, Nagapattinam, Trivandrum, Vijayawada, Guntur, Thirupathi, Nazarathpet, Kakinada, Kurnool, Kadapa, Nizamabad, Mahabubnagar, Karimnagar.