Grade Introduction:
En8D steel bar is a medium carbon steel grade of engineering steel that offers greater strength and hardness as compared to the low carbon grades. The formability and weldability of En8d are fair when using accepted shop practices. While machinability is good, this grade responds very well to forging and heat treating. It is one of the most used grades of carbon steel. People requiring better properties such as strength, etc generally go for alloy steel if En8d or equivalent grades are not suitable.
 
Grade Application:
Typical applications of En8d steel round bar include gears, shafts, axles, bolts, studs, crane wheels, and machine parts.
 
Equivalent grades:
Internal Standard
BS
DIN
IS
EN
SAE/AISI
EN8D
080A40
CK45
45C8
EN8D
1040, 1045
 
Addition to other grades:
MS, EN1A, EN3B, EN8, EN9, EN19, EN24, EN31, EN32B, EN36C, EN41B, EN43B, EN47, EN353, IS2062, 42Crmo4, HCHCR, OHNS, D2, D3, H-11, H-13, CW-1, M2, M35, M42, 2714, SKD-11, P20, P20+S, P20+Ni, SCM 420, ASTM SA-36, ASTM SA-105, SAE 1018, SAE 1020, SAE 4140, SAE 8620, 16MNCR5, 20MNCR5, C20, C35, C40, C45, C50, C60, CK45, 20C8, 40C8, 45C8, 55C8, C55MN75, SAE 52100, S40C, S355J2G3.
 
Our Supply Range:
 
Price List:
 
People also search as:
EN8D, EN8D Steel, EN8D Chemical composition, EN8D Mechanical properties, EN8D Equivalent Grades, EN8D Steel plate, EN8D Steel sheet, EN8D Manufacturers, EN8D Suppliers, EN8D Dealers, EN8D Stockist, EN8D Distributors, EN8D Wholesalers, EN8D Traders.
 
Chemical composition:
The following table shows the chemical composition of EN8D steel:
Element
C
Mn
P
S
Content(%)
0.40-0.45
0.70-0.90
0.045 Max
0.045 Max
 
Mechanical Properties:
MAX STRESS
700-850 N/MM 2
 
Yield Stress
465 n/mm 2  Min
(up to 19mm LRS)
0.2% Proof Stress
450 n/mm 2  Min
(up to 19mm LRS)
Elongation
16% Min
(12% if cold-drawn)
Impact KCV
28 Joules Min
(up to 19mm LRS
Hardness
201-255 Brinell
 
 
Hardness:
180-220

 

Heat treatment:
EN8D  can be tempered at a heat of between 550°C to 660°C (1022°F-1220°F), heating for about 1 hour for every inch of thickness, then cool in oil or water.
Normalizing of EN8 bright mild steel takes place at 830-860°C (1526°F-1580°F) then it is cooled in air.
Quenching in oil or water after heating to this temperature will harden the steel.

 

Hardening:
Heat the component slowly to 820-860°C and allow it to be heated through. Quench in oil or water.
 

 

Tempering:
Temper the EN8D component immediately after quenching whilst tools still hand warm. Re-heat the EN8D component to the tempering temperature then soak for one hour per 25 millimeters of total thickness (2 hours minimum) Cool in air. For most applications tempering of EN8D will be between 550-660°C.

 

Physical Properties:
Tensile Strength
90,000 psi
Yield Strength
50,000 psi
Elongation In 2”
20%
Reduction of Area
30%
Brinell Hardness
180-220
 
Thermal Properties:
 

 

Forging Properties:
Preheat the steel carefully, and then raise the temperature to 1050°C for forging. Do not forge below 850°C. After forging cool slowly, preferably in a furnace.
 
Stress Relieving:
 

 

Normalizing:
Normalizing of EN8D bright mild steel takes place at 830-860°C (1526°F-1580°F) then it is cooled in air.

 

Annealing:
Heat slowly to 680-710°C, soak well. Cool slowly in the furnace.

 

Density:
 
Machinability:
 
Welding:
Modern EN8D bright mild steel contains a lot less carbon than it uses to, this means that it is possible to weld pieces up to 18mm thick without preheating using MIG wire (SG2) or a 7018 electrode.
 
Over 18mm would require a pre-heat of 100°C (212°F) in order to prevent cracking.
 
Anneal afterward is recommended to prevent breaking.

 

Supply Cities:
Ahmedabad, Amaravathi, Ambattur, Bangalore, Belgaum, Chennai, Chittoor, Coimbatore, Dindigul, Mysore, Nellore, Hyderabad, Kochi, Mangalore, Tirupur, Tuticorin, Madurai, Andhra Pradesh, Karnataka, Puducherry, Kerala, Tamil Nadu, Telangana, Salem, Thanjavur, Trichy, Erode, Vellore, Ranipet, Sivakasi, Karur, Hosur, Nagercoil, Kanchipuram, Karaikudi, Neyveli, Cuddalore, Kumbakonam, Thiruvannamalai, Pollachi, Rajapalayam, Gudiyatham, Pudukottai, Vaniyambadi, Ambur, Nagapattinam, Trivandrum, Vijayawada, Guntur, Thirupathi, Nazarathpet, Kakinada, Kurnool, Kadapa, Nizamabad, Mahabubnagar, Karimnagar.