SAE52100 Round Bars, SAE52100 Round bar manufacturer, SAE52100 Rods Supplier, SAE52100 Stockiest, SAE52100 Dealers, SAE52100 Distributors, SAE52100 Whole sellers.
 
Grade introduction: 
AISI 52100 bearing steel is a high quality Alloy Bearing steel, It belong to a high carbon, chromium containing low alloy steel.. 52100 Oil Quenched & Tempered Hardness is 28-34 HRC. AISI 52100 steel Annealing delivery hardness less than 250HB.
AISI 52100 Alloy bearing steel properties is a chromium, manganese alloy steel specification. 52100 is equivalent to DIN 100Cr6, GB GCr15 steel. Most applications can replace each others.
 
Grade application : 
AISI 52100 steel is widely used for a variety of applications in the used to the bearings in rotating machinery. Typical applications such as valve bodies, pumps and fittings, the high load of wheel, bolts, double-headed bolts, gears, internal combustion engine. Electric locomotives, machine tools, tractors, steel rolling equipment, boring machine, railway vehicle, and mining machinery transmission shaft on the steel ball, roller and shaft sleeve, etc.
 
Equivalent grades : 
Country
USA
German
Japan
British
Standard
ASTM A295
DIN 17230
JIS G4805
BS 970
Grades
52100
100Cr6/1.3505
SUJ2
535A99/EN31
 
Addition to other grades
MS, EN1a, EN3b, EN8, EN8D, EN9, EN19, EN24, EN31, EN32B, EN36C, EN41B, EN43B, En47, EN353, IS2062, HCHCR, D2, D3, H-11, H-13, CW-1, OHNS, M2, M35, M42, 2714, SKD-11, P20, P20+s, P20+Ni, ASTM Sa-36, ASTM SA-105, SAE 1018, SAE 4140, SAE 8620, SCM420, 16MNCR5, 20MNCR5, C20, C35, C40, C45, C50, C60, CK45, 20C8, 40C8, 45C8, 55C8, C55MN75, 42CrMo4, S40C, S355J2G3.
 
Our Supply Range:
 
Price List:
 
People also search as:
SAE52100, SAE52100 Steel, SAE52100 Chemical composition, SAE52100 Mechanical properties, SAE52100 Equivalent Grades, SAE52100 steel plate, SAE52100 steel sheet, SAE52100 manufactures, SAE52100 suppliers, SAE52100 dealers, SAE52100 Stockiest, SAE52100 distributors, SAE52100 whole sellers, SAE52100 Traders.
 
Chemical composition: 
Standard
Grade
C
Mn
P
S
Si
Ni
Cr
Cu
Mo
ASTM A295
52100
0.93-1.05
0.25-0.45
0.025
0.015
0.15-0.35
0.25
1.35-1.60
0.30
0.10
DIN 17230
100Cr6/1.3505
0.90-1.05
0.25-0.45
0.030
0.025
0.15-0.35
0.30
1.35-1.65
0.30
JIS G4805
SUJ2
0.95-1.10
0.50
0.025
0.025
0.15-0.35
1.30-1.60
BS 970
535A99/EN31
0.95-1.10
0.40-0.70
0.10-0.35
1.20-1.60
 
Mechanical properties :
Properties
Metric
Imperial
Bulk modulus (typical for steel)
140 GPa
20300 ksi
Shear modulus (typical for steel)
80 GPa
11600 ksi
Elastic modulus
190-210 GPa
27557-30458 ksi
Poisson’s ratio
0.27-0.30
0.27-0.30
Hardness, Brinell
Hardness, Knoop (converted from Rockwell C hardness)
875
875
Hardness, Rockwell C (quenched in oil from 150°C tempered)
62
62
Hardness, Rockwell C (quenched in water from 150°C tempered)
64
64
Hardness, Rockwell C (quenched in oil)
64
64
Hardness, Rockwell C (quenched in water)
66
66
Hardness, Vickers (converted from Rockwell C hardness)
848
848
Machinability (spheroidized annealed and cold drawn. Based on 100 machinability for AISI 1212 steel)
40
40
 
Hardness:
 
Heat treatment properties : 
ASTM/AISI 52100 alloy bearing steel is heated at 816°C followed by quenching in oil. Before performing this process, it is subjected to normalizing heat treatment at 872°C followed by slowly cooling in order to reduce the machining stress.
 
Hardening : 
AISI 52100 alloy steel is hardened by cold working, or heating and quenching. It can be carburized at 913°C (1675°F) followed by quenching. It is again heated at 788°C (1450°F) followed by quenching for the second time.
 
Tempering :
Temper to desired hardness as indicated by tempering curves after water or oil quench.
 
Physical properties : 
Properties
Metric
Imperial
Density
7.81 g/cm3
0.282 lb/in³
Melting point
1424°C
2595°F
 
Thermal properties:
Properties
Metric
Imperial
Thermal expansion co-efficient (@ 23-280°C/73.4- 36°F, annealed)
11.9 µm/m°C
6.61 µin/in°F
Thermal conductivity (typical steel)
46.6 W/mK
323 BTU in/hr.ft².°F
 
Forging properties :
AISI 52100 alloy steel is forged at 927 to 1205°C, and should not be forged below 925ºC. A post-forge equalization treatment is recommended at 745ºC for 4-6 hours followed by air cooling for SAE/AISI 52100 steel.
 
Stress reliving : 
 
Normalizing : 
 
Annealing:
AISI 52100 alloy steel is annealed at 872°C (1600°F) followed by slowly cooling to reduce cold working or machining stress
 
Density :
Properties
Metric
Imperial
Density
7.81 g/cm3
0.282 lb/in³
 
Machinability : 
AISI 52100 alloy steel can be machined using conventional techniques. The machinability of this steel can be improved by performing sherardizing annealing process at 649°C (1200°F) before machining.
 
Welding:
 
Supply cities
Ahmedabad, Amaravathi, Ambattur, Bangalore, Belgaum, Chennai, Chittoor, Coimbatore, Dindigul, Mysore, Nellore, Hyderabad, Kochi, Mangalore, Tirupur, Thoothukudi, Madurai, Andhra Pradesh, Karnataka, Puducherry, Kerala, Tamil Nadu, Telangana, Salem, Thajavur, Tiruchurapalli, Comibatore, Erode,  Vellore, Ranipet, Sivakasi, Karur, Hosur, Nagercoil, Kanchepuram, Karaikudi, Neyveli, Cuddalore, Kumbakonam, Thiruvannamalai, Pollachi, Rajapalayam, Gudiyatham, Pudukottai, Vaniyambadi, Ambur, Nagapattinam, Trivandrum, Vijaywada, Guntur, Thirupathi, Nazarathpet, Kakinada, Kurnool, Kadapa, Nizamabad, Mahabubnagar, Karimnagar.