42CrMo4 Round Bars, 42CrMo4 Round bar manufacturer, 42CrMo4 Rods Supplier, 42CrMo4 Stockiest, 42CrMo4 Dealers, 42CrMo4 Distributors, 42CrMo4 Whole sellers.
 
Grade Introduction:
We are 42CrMo4 Round Bar manufacturers and manufacture a vast range of sizes and use only from prime quality billets and blooms as raw material. The range of products of 42CrMo4 Round Bar which we offer to our customers are of high quality and these round bars are used for making machineries and OEM Auto components. These products have been made keeping in mind the quality parameters which have been set by the industry in the market. 42CrMo4 Steel Round Bars are always supplied with the test certificates and can be supplied in bulk quantity as well as retail quantity as per customers requirements. 42CrMo4 round bars are supplied by us to various engineering and forging industries.
42CrMo4 Steel – SAE-AISI 4140 is classified as low alloy steel. Medium carbon steels are high strength steels which include EN19 as an important member in low alloy category. These steels show positive response to all variety of heat treatments. 42CrMo4 is a 1% chromium – molybdenum medium hardenability general purpose high tensile steel – generally supplied hardened and tempered in the tensile range of 850 –1000 Mpa (condition T). 42CrMo4 is a high quality, high tensile alloy steel usually supplied readily machinable in 'T' condition, giving good ductility and shock resisting properties combined with resistance to wear. We specialise in the supply of EN19, 4140, 42CrMo4 Hot Rolled Steel Round Bars.
 
Grade Application:
42CrMo4 alloy steel is widely used for engineering steel purpose, such as: making various kinds of machinery, automobile, mining spare part, the gearwheel of the engine, the driving gear of supercharger, the connecting rob, the pinchock under the high pressure, parts for power train applications, cold formed fastener components, shafts, gears, drill collars for the oil exploration, etc.
 
Equivalent grades:
AISI 4140, SAE 4140, 42CrMo4, 42CrMoS4, Din 1.7225
 
Addition to other grades:
MS, EN1a, EN3b, EN8, EN8D, EN9, EN19, EN24, EN31, EN32B, EN36C, EN41B, EN43B, En47, EN353, IS2062, HCHCR, D2, D3, H-11, H-13, CW-1, OHNS, M2, M35, M42, 2714, SKD-11, P20, P20+s, P20+Ni, ASTM Sa-36, ASTM SA-105, SAE 1018, SAE 4140, SAE 8620, SCM420, 16MNCR5, 20MNCR5, C20, C35, C40, C45, C50, C60, CK45, 20C8, 40C8, 45C8, 55C8, C55MN75, SAE52100, S40C, S355J2G3.
 
Our Supply Range:
 
Price List:
 
People also search as:
42CrMo4, 42CrMo4 Steel, 42CrMo4 Chemical composition, 42CrMo4 Mechanical properties, 42CrMo4 Equivalent Grades, 42CrMo4 steel plate, 42CrMo4 steel sheet, 42CrMo4 manufactures, 42CrMo4 suppliers, 42CrMo4 dealers, 42CrMo4 Stockiest, 42CrMo4 distributors, 42CrMo4 whole sellers,  42CrMo4 Traders.
 
Chemical composition:
The following table shows the chemical composition of 42CRMo4 steel:
Element
C
Mn
Si
P
S
Cr
Mo
Content(%)
0.38-0.45
0.60-0.90
0.40 max
0.035 max
0.035 max
0.90-1.20
0.15-0.30
 
Mechanical Properties:
Size Ø mm
Yield stress
Rp0.2,N/nn2, min
Ultimate tensile Stress,
Rm,N/nn2
Elongation
A5,%, min
Hardness HB
Toughness
KV, Joule, min.
<40
750
1000-1200
11
295-355
35 at 20 °C
40-95
650
900-1100
12
265-325
35 at 20 °C
>95
550
800-950
13
235-295
35 at 20 °C
 
Hardness:
295 – 355
 
Heat treatment:
42CrMo4 is alloy steel for quenching and tempering, which has a good combination of strength and toughness in the quenched and tempered condition. After the oil quenching, the steel will be through hardened up to ø60 mm bar diameter. The microstructure of larger dimensions is not fully marten site.
 
Hardening:
First quenching heated slowly to 880°C, Then after adequate soaking at this temperature quench in oil or water. Temper as soon as tools reach room temperature. Second quenching heat to 780-820°C, then quenching in oil or water.
 
Tempering:
Heat to 205-649°C, then cool in water or oil. normal delivery hardness 18-22 HRC.
 
Physical Properties:
 
Thermal Properties:
 
Forging Properties:
 
Stress Reliving:
 
Normalizing:
 
Annealing:
  • Heat steel 42CrMo4 forged steel slowly and thoroughly to 800-850°C;
  • Cool slowly in the furnace to the temperature 480°C;
  • Complete annealing the steel in the air.
 
Density:
7.85kg/m3 Tensile strength: 655 MPA
 
Machine ability:
 
Welding:
Engineering steel 42CrMo4 has only limited weldability. Preheating to 200-300°C is strongly recommended; the upper limit should not be exceeded because of risk for deterioration of the chrome layer. Alloy steel 42CrMo4 can be friction welded. However, precautions are necessary so as to limit the formation of undesirable micro structures in the welded zone.
 
Supply Cities:
Ahmedabad, Amaravathi, Ambattur, Bangalore, Belgaum, Chennai, Chittoor, Coimbatore, Dindigul, Mysore, Nellore, Hyderabad, Kochi, Mangalore, Tirupur, Thoothukudi, Madurai, Andhra Pradesh, Karnataka, Puducherry, Kerala, Tamil Nadu, Telangana, Salem, Thajavur, Tiruchurapalli, Comibatore, Erode,  Vellore, Ranipet, Sivakasi, Karur, Hosur, Nagercoil, Kanchepuram, Karaikudi, Neyveli, Cuddalore, Kumbakonam, Thiruvannamalai, Pollachi, Rajapalayam, Gudiyatham, Pudukottai, Vaniyambadi, Ambur, Nagapattinam, Trivandrum, Vijaywada, Guntur, Thirupathi, Nazarathpet, Kakinada, Kurnool, Kadapa, Nizamabad, Mahabubnagar, Karimnagar.